Structures by: Belov N. V.
Total: 277
Nd Al2.07 (B4 O10) O0.6
Al2.07B4NdO10.6
Doklady Akademii Nauk SSSR (1978) 241, 91-94
a=4.588Å b=4.588Å c=9.298Å
α=90° β=90° γ=120°
Er4 Ge3 O9 (O H)6
Er4Ge3H6O15
Doklady Akademii Nauk SSSR (1980) 251, 354-357
a=14.927Å b=10.732Å c=7.047Å
α=90° β=90° γ=90°
K Zn3 Mn2 Si12 O30
KMn2O30Si12Zn3
Kristallografiya (1971) 16, 721-724
a=10.52Å b=10.52Å c=14.22Å
α=90° β=90° γ=120°
K8 Yb3 (Si6 O16)2 (O H)
HK8O33Si12Yb3
Doklady Akademii Nauk SSSR (1981) 258, 1111-1115
a=6.808Å b=11.434Å c=11.449Å
α=88.52° β=90.91° γ=100.1°
Mg2 B6 O11 (H2 O)15
B6H30Mg2O26
Doklady Akademii Nauk SSSR (1969) 189, 1003-1006
a=8.28Å b=10.66Å c=6.4Å
α=99° β=108.5° γ=105.4°
Mg B12 O19 (H2 O)5
B12H10MgO24
Doklady Akademii Nauk SSSR (1979) 245, 1112-1115
a=11.56Å b=8.58Å c=8.67Å
α=90° β=102.74° γ=90°
(Co (N H2 N H C S N H2)3) Cl3 (H2 O)4
C3H23Cl3CoN9O4S3
Doklady Akademii Nauk SSSR (1981) 260, 98-102
a=13.507Å b=9.901Å c=16.131Å
α=90° β=90° γ=103.96°
Rh (S C N3 H5)3 Cl3
C3H15Cl3N9RhS3
Doklady Akademii Nauk SSSR (1980) 250, 361-364
a=15.396Å b=9.193Å c=11.496Å
α=90° β=90° γ=99.99°
Li3 Cr4 P O16 (H2 O)3
Cr4H6Li3O19P
Doklady Akademii Nauk SSSR (1981) 257, 619-621
a=9.635Å b=12.019Å c=7.696Å
α=90° β=110.4° γ=90°
Zn (H3 O) P O4
H3O5PZn
Doklady Akademii Nauk SSSR (1977) 236, 597-600
a=10.689Å b=10.689Å c=8.708Å
α=90° β=90° γ=120°
La2 V10 O28 (H2 O)20
H40La2O48V10
Doklady Akademii Nauk SSSR (1978) 242, 603-605
a=11.134Å b=16.18Å c=12.018Å
α=90° β=90° γ=101.7°
K2 Mn5 (Si12 O30) (H2 O)
H2K2Mn5O31Si12
Doklady Akademii Nauk SSSR (1977) 233, 1090-1093
a=10.457Å b=10.457Å c=14.238Å
α=90° β=90° γ=120°
Y2 (V10 O28) (H2 O)24
H48O52V10Y2
Doklady Akademii Nauk SSSR (1977) 235, 578-580
a=9.432Å b=9.874Å c=23.49Å
α=98.8° β=98° γ=90.1°
K2 Mn2 Zn4 Si4 O15
K2Mn2O15Si4Zn4
Doklady Akademii Nauk SSSR (1969) 185, 1045-1048
a=8.944Å b=15.834Å c=5.205Å
α=90° β=90° γ=90°
Ca (B2 O2 (O H)4)
B2CaH4O6
Doklady Akademii Nauk SSSR (1969) 189, 532-535
a=6.92Å b=12.35Å c=9.8Å
α=90° β=83° γ=90°
Li3 (B5 O8 (O H)2)
B5H2Li3O10
Doklady Akademii Nauk SSSR (1981) 257, 111-114
a=6.848Å b=6.848Å c=14.564Å
α=90° β=90° γ=90°
Cd Nd4 (Si O4)3 O
CdNd4O13Si3
Zhurnal Strukturnoi Khimii (Issue-No. from 1981) (1977) 18, 397-399
a=9.562Å b=9.562Å c=7.075Å
α=90° β=90° γ=120°
Na2 Ce4 Ti2 (Si O4)2 O6 (O H)2 (H2 O)8
Ce4H18Na2O24Si2Ti2
Doklady Akademii Nauk SSSR (1969) 185, 1289-1292
a=7.57Å b=13.98Å c=5.03Å
α=101.5° β=70.417° γ=101.5°
Ca Mn4 (Si O3)5
CaMn4O15Si5
Doklady Akademii Nauk SSSR (1977) 234, 586-589
a=7.6816Å b=11.818Å c=6.7073Å
α=92.355° β=93.948° γ=105.665°
Na2 Ca2 Fe Mn Zr2 (Si O4)4 (O H) F
Ca2FFeHMnNa2O17Si4Zr2
Doklady Akademii Nauk SSSR (1960) 130, 1333-1336
a=10.54Å b=9.9Å c=7.14Å
α=90° β=108.2° γ=90°
Na H Cd4 (Ge5 O15)
Cd4Ge5HNaO15
Doklady Akademii Nauk SSSR (1977) 234, 586-589
a=8.008Å b=12.224Å c=7.064Å
α=92.93° β=94.28° γ=106.2°
Ca Zn (Si O4) (H2 O)
CaH2O5SiZn
Doklady Akademii Nauk SSSR (1977) 237, 334-337
a=5.131Å b=15.928Å c=5.422Å
α=90° β=103.39° γ=90°
Li H Cd4 (Ge5 O15)
Cd4Ge5HLiO15
Doklady Akademii Nauk SSSR (1977) 234, 586-589
a=7.931Å b=12.269Å c=7.058Å
α=93° β=94.6° γ=105.75°
Cd (Ge O3)
CdGeO3
Zhurnal Strukturnoi Khimii (Issue-No. from 1981) (1981) 22, 199-200
a=10.204Å b=5.3852Å c=9.669Å
α=90° β=90° γ=102.23°
Na H Cd2 (Si3 O9)
Cd2HNaO9Si3
Doklady Akademii Nauk SSSR (1978) 240, 843-846
a=7.854Å b=6.982Å c=6.927Å
α=90.37° β=94.63° γ=102.71°
Na3 Sc (Si2 O7)
Na3O7ScSi2
Doklady Akademii Nauk SSSR (1969) 184, 337-340
a=5.354Å b=9.347Å c=13.089Å
α=90° β=90° γ=90°
Na8 (Al6 Ge6 O24) (C O3) (H2 O)2.48
CH4.96Al6Ge6Na8O29.48
Doklady Akademii Nauk SSSR (1977) 237, 585-588
a=12.913Å b=12.913Å c=10.493Å
α=90° β=90° γ=120°
Na4 Zr2 (Si O4)3
Na4O12Si3Zr2
Kristallografiya (1981) 26, 293-300
a=9.106Å b=9.106Å c=9.106Å
α=60.6° β=60.6° γ=60.6°
Na4 Zr2 (Ge O4)3
Ge3Na4O12Zr2
Doklady Akademii Nauk SSSR (1978) 238, 855-857
a=9.429Å b=9.429Å c=22.529Å
α=90° β=90° γ=120°
Na4 Zr2 (Si O4)3
Na4O12Si3Zr2
Doklady Akademii Nauk SSSR (1972) 205, 90-92
a=9.1Å b=9.1Å c=22.07Å
α=90° β=90° γ=120°
Cd3 (P O4)2
Cd3O8P2
Doklady Akademii Nauk SSSR (1978) 239, 1101-1102
a=15.65Å b=11.07Å c=7.56Å
α=90° β=90° γ=90°
Na4 Cd2 (Si3 O10)
Cd2Na4O10Si3
Doklady Akademii Nauk SSSR (1978) 238, 348-352
a=9.901Å b=5.85Å c=17.628Å
α=90° β=99.79° γ=90°
Na2 Cd3 (Si3 O10)
Cd3Na2O10Si3
Doklady Akademii Nauk SSSR (1977) 236, 866-868
a=16.426Å b=5.086Å c=10.958Å
α=90° β=94.2° γ=90°
C (N H2)3 I O3
CH6IN3O3
Doklady Akademii Nauk SSSR (1977) 236, 1361-1363
a=7.374Å b=10.281Å c=15.763Å
α=90° β=90° γ=96.12°
Na8 (Al6 Ge6 O24) (C O3) (H2 O)1.64
CH3.28Al6Ge6Na8O28.64
Doklady Akademii Nauk SSSR (1978) 243, 113-115
a=12.869Å b=12.869Å c=10.45Å
α=90° β=90° γ=120°
Rb I O3 (H I O3)2
H2I3O9Rb
Doklady Akademii Nauk SSSR (1980) 252, 615-618
a=8.25Å b=8.238Å c=8.21Å
α=108.55° β=120.16° γ=94.49°
Na I O3
INaO3
Doklady Akademii Nauk SSSR (1979) 249, 613-616
a=6.3959Å b=5.7475Å c=8.1286Å
α=90° β=90° γ=90°
Mg (I O3)2 (H2 O)4
H8I2MgO10
Doklady Akademii Nauk SSSR (1979) 247, 106-109
a=8.321Å b=8.501Å c=6.636Å
α=90° β=90° γ=100.36°
Al (I O3)3 (H2 O)8
AlH16I3O17
Doklady Akademii Nauk SSSR (1979) 247, 360-363
a=7.473Å b=8.392Å c=13.574Å
α=89.93° β=87.62° γ=63.58°
Ca3 Cl2 (Si O4)
Ca3Cl2O4Si
Doklady Akademii Nauk SSSR (1970) 193, 1048-1051
a=9.79Å b=6.76Å c=10.96Å
α=90° β=105.4° γ=90°
K2 Cr3 O10
Cr3K2O10
Doklady Akademii Nauk SSSR (1978) 239, 1343-1345
a=7.334Å b=9.613Å c=17.32Å
α=90° β=90° γ=128.9°
Cu S O4 (C O (N H2)2 )3
C3H12CuN6O7S
Kristallografiya (1977) 22, 994-1003
a=13.004Å b=9.268Å c=8.873Å
α=90° β=90° γ=90°
Na2 (Ti O) (Ge O4)
GeNa2O5Ti
Doklady Akademii Nauk SSSR (1970) 190, 91-93
a=6.67Å b=6.67Å c=5.56Å
α=90° β=90° γ=90°
In2 Ge2 O7
Ge2In2O7
Doklady Akademii Nauk SSSR (1973) 213, 837-839
a=6.59Å b=4.91Å c=8.72Å
α=90° β=90° γ=102°
Na2 Fe3 (P O4)3
Fe3Na2O12P3
Doklady Akademii Nauk SSSR (1977) 236, 1123-1126
a=10.923Å b=6.5Å c=12.538Å
α=90° β=90° γ=90°
Na12 Ca6 Fe3 Zr3 (Si24 O66) (O H)5 Cl
Ca6ClFe3H5Na12O71Si24Zr3
Kristallografiya (1972) 17, 1119-1123
a=14.248Å b=14.248Å c=30.02199Å
α=90° β=90° γ=120°
Sc2 Ge O5
GeO5Sc2
Kristallografiya (1974) 19, 1081-1083
a=10.927Å b=10.656Å c=10.486Å
α=90° β=90° γ=93.5°
Na2 U O2 Si O4
Na2O6SiU
Kristallografiya (1974) 19, 958-963
a=12.718Å b=12.718Å c=13.376Å
α=90° β=90° γ=90°
Ca (B2 O2 (O H)4)
B2CaH4O6
Kristallografiya (1976) 21, 592-594
a=10.026Å b=4.44Å c=9.558Å
α=90° β=90° γ=91.31°
Ca4 Mn3 B3 O12 C O3
CB3Ca4Mn3O15
Kristallografiya (1975) 20, 152-155
a=10.606Å b=10.606Å c=5.879Å
α=90° β=90° γ=120°
Na Cs2 (Al F6)
AlCs2F6Na
Kristallografiya (1978) 23, 42-46
a=10.697Å b=10.561Å c=6.176Å
α=90° β=90° γ=109.73°
Na2 (Be F4)
BeF4Na2
Doklady Akademii Nauk SSSR (1965) 163, 94-96
a=10.181Å b=5.61Å c=4.447Å
α=90° β=90° γ=90°
Na2 Ti2 O3 (Si O3)2
Na2O9Si2Ti2
Doklady Akademii Nauk SSSR (1969) 186, 820-823
a=14.518Å b=8.976Å c=5.081Å
α=90° β=90° γ=90°
CALCIUM STRONTIUM SILICATE
CaO4SiSr
Doklady Akademii Nauk SSSR (1982) 267, 641-644
a=20.871(2)Å b=9.496(1)Å c=5.600(1)Å
α=90° β=90° γ=90°
CALCIUM STRONTIUM SILICATE
CaO4SiSr
Doklady Akademii Nauk SSSR (1982) 267, 641-644
a=20.871(2)Å b=9.496(1)Å c=5.600(1)Å
α=90° β=90° γ=90°
Ca (B2 O (O H)6) (H2 O)2
B2CaH10O9
Doklady Akademii Nauk SSSR (1973) 208, 1082-1085
a=7.875Å b=6.534Å c=8.104Å
α=111.53° β=111.33° γ=72.7°
Ca1.2 Mg1.7 Al3.9 Si1.2 O10.3 (O H)1.7
Al3.9Ca1.2H1.7Mg1.7O12Si1.2
Doklady Akademii Nauk SSSR (1961) 137, 167-170
a=5.18Å b=9.09Å c=18.89999Å
α=90° β=85° γ=90°
Na2 Ca (Al2 Si3 O10)2 (H2 O)6
Al4CaH12Na2O26Si6
Doklady Akademii Nauk SSSR (1972) 203, 1299-1301
a=13.4Å b=13.4Å c=6.63Å
α=90° β=90° γ=90°
Ca Be2 (P O4)2
Be2CaO8P2
Doklady Akademii Nauk SSSR (1960) 135, 587-590
a=8.29Å b=8.8Å c=7.81Å
α=90° β=90° γ=90°
Dy4.67 (Ge O4)3 O
Dy4.67Ge3O13
Kristallografiya (1972) 17, 490-493
a=9.2Å b=9.2Å c=6.808Å
α=90° β=90° γ=120°
Ce4.67 Si3 O13
Ce4.67O13Si3
Kristallografiya (1972) 17, 490-493
a=9.736Å b=9.736Å c=7.116Å
α=90° β=90° γ=120°
Cs In (Se O4)2 (H2 O)2
CsH4InO10Se2
Doklady Akademii Nauk SSSR (1975) 224, 335-337
a=9.439Å b=7.159Å c=14.84Å
α=90° β=90° γ=105.03°
Na Gd (Si O4)
GdNaO4Si
Kristallografiya (1970) 15, 1066-1067
a=11.63Å b=11.63Å c=5.41Å
α=90° β=90° γ=90°
Na2 Zn (Si2 O6)
Na2O6Si2Zn
Kristallografiya (1969) 14, 1060-1062
a=21.503Å b=7.12Å c=7.4Å
α=90° β=90° γ=90°
Cu3.75 Hg1.75 Sn2 S8
Cu3.75Hg1.75S8Sn2
Kristallografiya (1977) 22, 175-177
a=5.542Å b=5.542Å c=10.908Å
α=90° β=90° γ=90°
Ca (Al4 O7)
Al4CaO7
Kristallografiya (1970) 15, 1140-1143
a=12.866Å b=8.879Å c=5.44Å
α=90° β=106.75° γ=90°
Ca3 Mg (B O3)2 (C O3) (H2 O)0.125
CH0.25B2Ca3MgO9.125
Doklady Akademii Nauk SSSR (1974) 218, 576-579
a=14.69Å b=14.69Å c=14.69Å
α=90° β=90° γ=90°
Ba Cl2 (H2 O)2
BaCl2H4O2
Kristallografiya (1980) 25, 1064-1065
a=6.717Å b=10.9Å c=9.696Å
α=90° β=132.7° γ=90°
((N H2 C O N H2)6 Cr) (Co (N H3)2 (N O2)4)3 (H2 O)3
C6H24Co3CrN30O33
Doklady Akademii Nauk SSSR (1979) 244, 358-361
a=24.78Å b=24.78Å c=13.195Å
α=90° β=90° γ=120°
Na (Sr.77 Ba.20) (P O4) (H2 O)9
Ba0.2H18NaO13PSr0.77
Doklady Akademii Nauk SSSR (1981) 261, 619-623
a=10.559Å b=10.559Å c=10.559Å
α=90° β=90° γ=90°
Na H Cd2 (Si3 O9)
Cd2HNaO9Si3
Doklady Akademii Nauk SSSR (1973) 212, 1105-1108
a=7.847Å b=6.98Å c=6.92Å
α=90.4° β=94.6° γ=102.8°
Na Cd4 (Ge5 O14 (O H))
Cd4Ge5HNaO15
Doklady Akademii Nauk SSSR (1973) 213, 1300-1303
a=7.064Å b=8.008Å c=12.591Å
α=68.9° β=95.95° γ=94.466°
Gd Al3 (B O3)4
Al3B4GdO12
Doklady Akademii Nauk SSSR (1981) 261, 361-365
a=7.227Å b=9.315Å c=16.184Å
α=90° β=90.57° γ=90°
Ca2 Ga (Ga Ge) O7
Ca2Ga2GeO7
Doklady Akademii Nauk SSSR (1981) 260, 1363-1366
a=7.896Å b=7.896Å c=5.207Å
α=90° β=90° γ=90°
Y Al3 (B O3)4
Al3B4O12Y
Zhurnal Strukturnoi Khimii (Issue-No. from 1981) (1981) 22, 196-198
a=9.295Å b=9.295Å c=7.243Å
α=90° β=90° γ=120°
K Ca2 (Be2 Al) (Si12 O30)
AlBe2Ca2KO30Si12
Trudy Instituta Kristallografii, Akademiya Nauk SSSR (1951) 6, 83-140
a=10.43Å b=10.43Å c=13.85Å
α=90° β=90° γ=120°
K2 Sm F5
F5K2Sm
Doklady Akademii Nauk SSSR (1973) 212, 357-359
a=10.8Å b=6.62Å c=7.51Å
α=90° β=90° γ=90°
K2 Zr (Si3 O9)
K2O9Si3Zr
Kristallografiya (1977) 22, 59-65
a=6.926Å b=6.926Å c=10.177Å
α=90° β=90° γ=120°
Ca0.67 Cd0.33 (C O3)
CCa0.67Cd0.33O3
Doklady Akademii Nauk SSSR (1979) 245, 1099-1101
a=4.968Å b=4.968Å c=16.826Å
α=90° β=90° γ=120°
Ca3 Ge ((Ga2 Ge) Ge2 O14)
Ca3Ga2Ge4O14
Doklady Akademii Nauk SSSR (1981) 260, 1363-1366
a=8.076Å b=8.076Å c=4.974Å
α=90° β=90° γ=120°
(Fe0.1 Mg0.9) (Ca0.1 Fe0.5 Mg0.4) (Si2 O6)
Ca0.1Fe0.6Mg1.3O6Si2
Doklady Akademii Nauk SSSR (1981) 258, 99-102
a=9.713Å b=8.931Å c=5.231Å
α=90° β=108.61° γ=90°
Mg0.208 Fe.955 Ti.833 O3
Fe0.955Mg0.208O3Ti0.833
Doklady Akademii Nauk SSSR (1978) 242, 330-332
a=5.068Å b=5.068Å c=13.932Å
α=90° β=90° γ=120°
Ca5 Na4 K2 (Si12 O30) (O H)4
Ca5H4K2Na4O34Si12
Doklady Akademii Nauk SSSR (1969) 185, 672-674
a=18.74Å b=7.19Å c=12.33Å
α=90° β=112° γ=90°
K Er (P O3)4
ErKO12P4
Doklady Akademii Nauk SSSR (1980) 251, 1392-1395
a=10.8Å b=8.859Å c=12.7Å
α=90° β=128.89° γ=90°
Yb4 Ge3 O9 F6
F6Ge3O9Yb4
Doklady Akademii Nauk SSSR (1980) 250, 857-861
a=14.866Å b=10.694Å c=7.028Å
α=90° β=90° γ=90°
Ba5 (Si4 O12) (O H)2
Ba5H2O14Si4
Doklady Akademii Nauk SSSR (1970) 194, 83-86
a=7.745Å b=7.745Å c=11.68Å
α=90° β=90° γ=90°
Na Ba3 (Si2 O7) (O H)
Ba3HNaO8Si2
Doklady Akademii Nauk SSSR (1971) 200, 591-593
a=5.791Å b=5.791Å c=14.748Å
α=90° β=90° γ=120°